EVA FILM for manufacturing solar panel

product model:

JCC  EVA Solar cell encapsulation film model:

Fast Cure:JCC-105; High penetration type:JCC-105 -T

product specification :

1,Lamp shape:EVA Ultra Barrier Solar Films are Double stripe type;and also

can manufacture products of other stripes according to customers’ needs.

2,Product thickness:We can supply different thickness arranging from

0.30-0.80mm, the thickness of conventional product are 0.40mm and 0.50mm,

thickness tolerance:±0.03mm.

3,Product width: any width below 2000mm, and the normal width: 350,550,

680,810,820,980,1000mm, width tolerance: ±3mm

4,Length of each roll:100m,Tolerance:±1 m can manufacture according

to customers’ needs.

The products should be in the original packaging before being used ,and must be stored as the above requirements. At the same time, there was prevented from harmful gas, flammable and corrosive chemical products. Product package should be at least 10 cm from the ground,And the distance shall be not less than 50 cm from wall, heat source, the electrical equipment, etc .The all items (include reliability) of products must be tested when it over the storage life,when they are qualified and then the product can be used.

Curing process conditions:

JCC-105/ JCC-105-T Suggested laminating temperature:140±2℃(can

change according to customers’ needs)

pumpdown time 4-6min

Laminated time 8-10min

To ensure the quality of modular package, we suggest that after the

calibration of laminating machine temperature, following the technological

conditions can ensure EVA film crosslinking degree is above 80% and then

ensure the quality.If you want to increase the degree of crosslinking layer , you can

be appropriately raise the temperature or pressure holding time

1, JCC-105/JCC-105-T:

Laminating machine temperature 138-142℃,vacuumize 5min,forcing

60s,Laminated keep 8-10min.

2,Laminating instructions:

(a),Laminating conditions according to the performance of the laminating

machine. According to the temperature characteristics of each

laminating machine,tracking test must at any time,Selection of crosslinking degree between 70% ~ 70% after curing of process

conditions is preferred.Crosslinking degree is too low or too high can

lead to poor late aging performance.

(b),If laminating machine working environment temperature is different,

process conditions should be adjusted, specific to each laminating

machine parameters shall prevail.

3, After the completion of the laminated,Should after the temperature of

laminated good components down natural 80 ℃ and then Then open

the warm cloth , remove the components to trimming and deflashing .