Specifications

Boron nitride ceramic
fessional manufacturer
2.CE quality
3.high flexural strengt
4.as customized

  high quality  Boron nitride ceramic parts  with best price 

 

Boron Nitride ceramic are made by hot pressing hexagonal Boron Nitride powders. The color of BN products is milky, true density is 2.27g/cm , Mohs value is 2, they have a high melting point(sublimate point is 3000°C). When in a condition of inert atmosphere, their maximum service temperature can reach to 2800°C. Their thermal conductivity is 25W/(m·K), similar to stainless steel.And coefficient of liner  And coefficient of liner expansion is between 2.0×10 /°C to 6.5×10 /°C.

 

the features of the  Boron nitride ceramic parts

 

They have a high quality of heat-resistance and shock-resistance, and they can work efficiently after several hundred of 1000°C←→20°C cycles. Their oxidation resistance is poor, and their chemical properties are stable, they have a high corrosion-resistance of acid, alk, molten metal and glass. BN products cannot have chemical reaction with most molten metals, such as Cu, stainless steel, Fe, Sn, Zn and Sb. Mechanical strength is low, just a little more than that of graphite, volume resistance is between 25~1050°C,10-6~10-6n·cm, they are good insulators. Electric breakdown strength is between 30 kV/cm to 40 kV/cm, which is three times than that of aluminum oxide. Thermo compression products are distinctly anisotropic, they can be used to finish cut, and the precision of lathe can reach to 0.01mm.

 

 

The technical paramaters 

 

Grade	BN99	CABN	ALBN	ZSBN	ZABN	SBN
Compositions	BN>98.5%	BN>97.5%	AlN+BN	ZrO2+BN	ZrO2+AlN+BN	SiC+BN
Binder	B2O3	CaB2O3	AlBO3	B2O3	AlBO3	AlBO3
Density(g/cm3)	1.95~2.0	2.0~2.1	2.6	2.9~3.0	3.2~3.3	2.4~2.6
25°C           Volume Resistivity(Ω·cm)	>1014	>1013	>1014	>1012	>1012	>1012
Max. Service Temp. (°C)  Oxygen Inert Gas High Vacuum	900 2400 2200	900 2400 2200	900 2100 1900	1000 1800 1800	900 1800 1800	900 1700 1700
Three-point  Flexural Strength(Mpa)	30	70	130	120	130	91
Compressive Strength(Mpa)	100	100	250	280	300	300
Coefficient of Thermal Expansion 25~1000°C(10-6/K)	1.5	2.0	4.5	5.0	5.0	4.0
Thermal Conductivity(W/mK)	15	20	50	20	40

 

 

Typical Boron Nitride Applications:

1.Electronic Parts - heat sinks, substrates, coil forms, prototypes

2.Boron doping wafers in silicon semiconductor processing

3.Vacuum melting crucibles

4.CVD crucibles

5.Microcircuit packaging

6.Sputtering targets

7.High precision sealing, brazing, and metallizing fixtures

8.Microwave tubes

9.Horizonatal caster break rings

10.Low friction seals

11.Plasma arc insulators

12.High temperature furnace fixtures and supports 

 