STA High temperature silicon carbide graphite crucibles for non ferrous metal

1. Shape: According to your drawing.

2. Material: graphite+SiC

3. Process:mold Isostatic pressing

4. Application: for melting iron, aluminum and alloys

1.Thermal stability: We make special design to assure the quality accordig to the instant temperature changing working condition.

2.Corrosion resistance: Precise design extends the ability of corrision resistance of the crucible.

3.Impulsion resistance: Duratight graphite crucible can stand very strong heat impulsion, so it can be freely used in any technic process.

4.Acid resistance: Impregnation of special stuff can improve the quality of the crucible and its outstand in the acid resistance. As a result, it can prolong the work life of the graphite crucible.

5.Fine thermal conductivity: High content of fixed carbon ensures the good thermal conductivity, shorten the dissolving time and lower the cost of the oil and other energy obviously.

6.Control of metallic pollution : Strict control of the contents assures that there is no pollution to the metal during dissolving.

7.Quality stability: High-pressure manufacturing method and quality control system can pledge the quality stability better.

Chemical Composition

C %	SiC%	AL2O3 %	SIO2%
45%-50%	20%-30%	10%-12%	15-25%

The specification of sic graphite crucible:

Content of C	≥ 45
Density(g/cm3)	≥ 1.85
Apparent porosity (%)	≤ 21
pressive strength(Mpa)	≥ 25
refractability	≥ 1400C(melting alumina) ≥ 1550C(melting copper)
rupture strength(Mpa)	9-12
diathermancy	3.0-3.7×10-6/C
C	45-50%
Sic	20-30%
Sio2	15-25%
Si	3-8%
A12O3	10-12%