extruded uhmw-pe pipe
USD $10 - $50 /Meter
Min.Order:200 Meters
Shandong Buoy & Pipe Industry Co., Ltd.
Extruded UHMWPE Pipes:
Company: Shandong Buoy&Pipe Industry Co., Ltd.
Products: UHMWPE (Ultra high molecular weight polythene) pipe
Production Capability: 25 production lines, with annual production capability of 10,000 tons
Business type: manufacturer and exporter
OEM service: Available
Specification: DN77-DN1200
WT: 6mm-50mm
Length: 1m-12m
Benefits of UHMWPE pipes:
Longer Life
With a wear resistance 4 to 7 greater than Q235 Steel or 10 times that of HDPE (PE100) pipes under the same operating conditions, UHMWPE Pipe will give you far superior life under most operating conditions.
Lower Maintenance Costs, Less Maintenance Time, Less Downtime, Less Loss of Production
The far superior collaboration of wear resistance and weight reduction (0.93 SG) means the time between pipe replacements and/or rotations can be increased whilst simultaneously reducing installation management constraints of lifting gear and excavation requirements.
Reduced Pumping Costs
Along with the benefits mentioned above, UHMWPE Pipes also offer significant cost savings through increased pumping efficiency. With a surface roughness of 0.00022mm UHMWPE Pipe is extremely smooth and has resultant properties superior to PTFE (Teflon). Quantifying by example UHMWPE has a friction coefficient of 0.05, compared to 0.28 for HDPE or 0.58 for Steel (ISO 8295).
This means less friction, less pressure loss and greatly reduced energy inputs to deliver the same result.
Chemical and Corrosion Resistance
With chemical resistance second only to PTFE (Teflon), UHMWPE pipe will offer superior life to other pipeline products in acidic or corrosive applications under 85 degrees C.
Comapny: Shandong Buoy&Pipe Industry Co.,Ltd
Shandong Buoy&Pipe Industry Co.,Ltd is specialized in manufacturing UHMWPE products(UHMWPE pipe and UHMWPE buoy).
Production Equipments: 25 Production Lines
Introduction of UHMWPE pipe:
Ultra-high molecular weight polyethylene (UHMWPE) is a new kind of engineering thermoplastics with more than 3 million viscosity-average molecular weight. Ultra-high molecular weight polyethylene pipe has superior performance over conventional HDPE pipe such as very high wear resistance, impact resistance, excellent resistance to internal pressure strength, resistance to environmental stress cracking, intrinsically self-lubricating, anti-adhesion, low temperature resistance and excellent chemical resistance
UHMWPE Material: 3.5 Millon China Material or Ticona GUR material
UHMWPE Pipe Specification:
UHMWPE Pipe Connection
UHMWPE Pipe Images:
The UHMWPE pipes will be packed by poly bags, shipped by 20GP container, 40GP container, 40HQ container
Q: What's the difference between HDPE pipe and UHMWPE pipe?
A: the molecular wieght for HDPE pipe is only 30,000-50,000, however, the UHMWPE pipes is 3.5 million to 9.2 million. The higher molecular weight enables UHMWPE pipes to have a much better quality than HDPE pipes.
Q: What's the advantages of UHMWPE pipes compared with HDPE pipes?
A: a) Wear Resistance: the wear resistance of UHMWPE material is the top among engineering plastics, It is 10 times better than HDPE material;
b) Higher pressure bearing capability: with 2 times better of tensile strength than HDPE pipes, the UHMWPE pipes could bear higher working pressure. In this case, with the same internal diameter, the UHMWPE pipes could have thinner wall thickness to bear same working pressure.
Q: What's the advantages of Shandong Buoy&Pipe Industry Co.,Ltd?
A: a). Our company began to produce UHMWPE pipes since 2003, with 25 production lines, we have annual production capacity of 10,000 tons.
b).Various Specifications: diameter ranging from I.D77mm to I.D1200mm. We are specialised in research and production of large diameter UHMWPE pipes.
c). Good quality: 100% virgin UHMWPE material is used, China material with 3.5 million,Ticona GUR 4120 and GUR4150 material also availabel for pipe production.
Performance comparison of UHMW-PE with other materials
Item | Experimental methods | Units | UHMWPE | PA66 | PVC | PE | Steel Pipe |
Average molecular weight | GB1841 | 3.5×106 | 5×105 | ||||
Density | GB1033 | G/Cm3 | 0.935 | 1.13-1.15 | 1.4 | 0.945 | 7.8 |
Water absorption | ASTMD-570 | % | 0.01 | 3.8 | 0.07-0.4 | 0.01 | |
Melting Point | ISO11357.3 | 136 | 255 | 160 | 129 | ||
Heat distortion temperature0.46MPa | GB1634 | 85 | 182-224 | 54-73 | 71 | ||
Linear expansion coefficient | ASTMD-696 | 10-4/ | 1.5 | 0.8 | 1.2 | ||
Tensile strength | GB/T1040 | MPa | 39.2 | 61 | 40 | 25 | |
Tensile yield stress | GB/T1040 | MPa | 22 | 20 | |||
Tensile elongation at break | GB/T1040 | % | ≥350 | 60-300 | 60-120 | ≥350 | |
The impact on the Gap of simply supported beam | GB/T1043 | KJ/m | Continuously | 5.9-10.8 | 10 | 27 | |
Rockwell hardness | GB/T9342 | 40 | 85-120 | 33 | |||
Friction coefficient | Three petrochemical Law | 0.05-0.11 | 0.37 | 0.4-0.6 | 0.4 | 0.58 | |
Wear rate | Three petrochemical Law | % | 21 | 100 | 210 | 210 | 140 |
Scaling | Non- scaling | Scaling | |||||
Corrosion-resistant | Merit | Average | Average | Average | Average |