China Refractory Ceramic Fiber Board For Heat Resistant :

$China Refractory Ceramic Fiber Board For Heat Resistant$

Specification:

Thickness	Size
3mm-50mm	900x600mm/600x400mm/1200x600mm/1200x1000mm

Product Description:

IKINGWOOL ceramic fiber boards are an ideal thermal insulation , fire-proofand sound-absorbing material. The ceramic fiber board is composed of long, flexible, interwoven fibers manufactured by the blownand the spunprocess yielding a strong, light weight, durable blanket for applications in a temperature range from 1100° C (2012° F ) to 1430° C (2600° F).The ceramic fiber blanket is completely inorganic and is needled to provide exceptional handling strength, used in a variety of heat processing applications.

Advantages:

Low density and low thermal conductivity

Resilience and resistance to thermal shock

Excellent chemistry quality

Flexible and easy to cut or install

Aluminosilicate Refractory Material Ceramic Fiber Blanket

Product Application:

Ceramic Fiber Wool is widely used for industrial furnace heat treatment, direct exposure to heat as furnace hot face lining, high temperature filter material, heat treatment insulation, and expansion joints.

$China Refractory Ceramic Fiber Board For Heat Resistant$

Notes:

Common grade	1100ºC(2012 ° F)
Standard grade	1260ºC(2300 ° F)
High Pure grade	1260ºC (2300 ° F)
High Alumina grade	1360ºC(2480 ° F)
Zirconia grade	1430ºC(2600 ° F)

Company Information

Manufacturing Process:

$China Refractory Ceramic Fiber Board For Heat Resistant$

IKING Ceramic Fiber Board Laboratory:

$China Refractory Ceramic Fiber Board For Heat Resistant$

Technical Parameters:

Description		Common	Standard	High Purity	High Alumina	Zirconia
Maximum temperature (°C)		1100	1260	1260	1360	1430
Working Temperature (°C)		< 1000	1050	1100	1200	1350
Color		white	white	white	white	white
Density (kg/m3)		96-128	96-128	96-128	128-160	128-160
Shrinkage(%)of heating 24 hours		-4	-3	-3	-3	-3
(as density 128 kg/m3)		(1000°C)	(1000°C)	(1100°C)	(1250°C)	(1350°C)
Thermal conductivity (w/m.k)(Density 128 kgs/ m3)		0.09(400°C)	0.09(400°C)	0.09(400°C)	0.12(600°C)	0.16(800°C)
Thermal conductivity (w/m.k)(Density 128 kgs/ m3)		0.16(800°C)	0.16(800°C)	0.16(800°C)	0.20(1000°C)	0.20(1000°C)
Tensile strength (MPa)		0.04	0.04	0.04	0.04	0.04
(density as 128kg/m3)		0.04	0.04	0.04	0.04	0.04
Chemical composition(%)	AL2O3	44	46	47-49	52-55	39-40
	AL2O3 & SIO2	96	97	99	-	-
	AL2O3 & SIO2 & ZrO2	-	-	-	99	99
	ZrO2	-	-	-	15-17	15-17
	Fe2O3	<1.2	<1.0	0.2	0.2	0.2
	Na2O & K2O	≤0.5	≤0.5	0.2	0.2	0.2