Specifications

Spinel Alumina Magnesia Fire Brick
1.Good alkali resistance
2.Good corrosion resistance
3.High refractoriness under

  Magnesia Spinel Alumina Magnesia Fire Brick

 

 

 

Features

1. Good slag resistance

2. Excellent corrosion resistance

3. High refractoriness under load

 

Applications

Magnesia alumina spinel brick is widely used in transition zone of large dry-process cement rotary kiln, lining of ladle,and roof of EAF, etc.

 

Physical properties and chemical composition 

Item	LMLJ-80		LMLJ-75
	Standard	Typical Value	Standard	Typical Value
MgO, %	≥80	85.5	≥75	81.2
Al2O3 , %	8~15	10.2	8~15	9.83
apparent porosity, %	≤17(18)	16	≤18(19)	16
0.2MPa refractoriness under load °C	≥1700	1800	≥1650	1750
cold crushing strength ,MPa	≥40	57	≥40	68
Thermal expansion(1100°C,water cooling), times	≥20	≥20	≥5	≥16

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 Brief Introduction of Sunrise

 

 

Zhengzhou Sunrise Refractory Co., Ltd. is mainly engaged in the production and development of refractory 

 

materials for glass , petrochemistry, metallurgy, construction and nonerrous metal industries. Our main

 

products include fused cast AZS 33, 36,41, fused cast αβ alumina brick, crucibles, furnace fireclay bottom 

 

block, silica, high alumina, magnesia, corundum, chrome, zircon, mullite, zirconia mullite, silicon carbide, 

 

sillimanite, alumina bubble bricks, various insulation bricks, and ceramic fiber products,etc.