Specifications

1.featuring high strength
2.featuring high strength
3.good resistance to thermal shock
4.Sialon bonded corundum brick

Silicon carbide bricks have been developed and produced by Zhengzhou Sunrise Technology Co., Ltd. featuring high strength, high thermal conductivity, and good resistance to thermal shock, slag corrosion and abrasion as well as long service life. It is the best choice as the material used for blast furnace and boiler of fluidization furnace in I & S and power industries.

Sialon bonded corundum bricks featuring high strength, high temperature creep resistance, good abrasive resistance, and good alkali and slag corrosion resistance as well as long service life, etc. Excellent performance has been achieved in blast furnace in I & S industry.

Silicon Carbide Brick and Sialon Bonded Corundum Brick for Blast Furnace

Item				Sialon Sialon bonded corundum brick
SiC,  %  ≥		72	70	80 (Al2O3)
Si3N4, %  ≥		20	5 (N)	5 (N)
Fe2O3, %  ≤		0.7	0.7	0.7
g/cm3,  ≥ Bulk density		2.65	2.65	3.1
%,≤ Apparent porosity		16	16	16
MPa,  ≥ CCS		150	150	120
MOR	≥ Room temp.	42	42	12
	≥ 1400°C×0.5hrs	45	42	20
°C  ≥ (0.2MPa, 0.6%) Refractoriness under load		1700	1700	1700
≥(1100°C) Thermal shock resistance, cycles (Water quenching at 1100°C)		30	30	30
Application		Mainly used for lower part of stack, bosh, belly lining of blast furnace and boiler linings of fluidization furnace, etc.	Mainly used for lower part of stack, bosh, belly lining of blast furnace	Mainly used for ceramic cup of blast furnace and other parts such as bosh and belly area