Wear-Resistance bricks are made of raw materials such as high-grade bauxite and Australia imported zircon sand, which are melted and founded in high temperature electric furnace. It is mainly used in areas that require high abrasion and temperature resistance, such as gliding rail bricks in steel pusher metallurgical furnaces, the tapping platform (tapping spout) for tapping platform (tapping spout) style walking beam furnaces, and also as the interior for destructors.

( % )Chemical Composition
SiO2		19
Al2O3		73
Na2O		1.0
ZrO2		5.5
Others		1.5
Physical Properties		-
True density(g/cm3)		3.54
Cold crushing strength(Mpa)		>350
(%)Thermal expansion rate(%) 1150°C		0.8
Thermal Conductivity(500-1500°C)		4.6w/m.0k
Porosity		<4%
Bulk density (g/cm3)	PT	≥3.0
	WS	≥3.2
Crystalline hpase composition( % )		-
Corundum		38%
Porzite		40%
Glass phase		17%
Baddeleyite		5%