Specifications

1.high temperature resistance
2.long service life
3.large bulk density
4.low iron content

Wear-Resistance bricks are made of raw materials such as high-grade bauxite and Australia imported zircon sand, which are melted and founded in high temperature electric furnace. It is mainly used in areas that require high abrasion and temperature resistance, such as gliding rail bricks in steel pusher metallurgical furnaces, the tapping platform (tapping spout) for tapping platform (tapping spout) style walking beam furnaces, and also as the interior for destructors.

Physical and chemical index:

 

Item			Behaviors TY-GM5
			Special	Typical
Chemical Composition %	Al2O3		71-74	73
	ZrO2		4.5-6	5.5
	SiO2		17-20	19
	Fe2O3		≤0.5	0.5
	Na2O		≤1.0	1.0
	CaO		≤0.5	0.5
Apparent Prosity (%)			5-8	<8
True density g/cm3			≥3.0	3.54
Cold Crushing Strength Mpa			≥250	350
Hot Crushing Strength 1300°C Mpa				45
Line Expansion 1150°C %				0.9
Thermal conductivity 1250 °C: W/MK				4.6
Bulk Density (g/cm3)		PT(RN)		≥3.0
		WS(VF)		≥3.2
Crystallographic analysis %	Corundum		39
	Mullite		41
	Glass Phase		15
	Baddeleyite		5