Specifications

Excellent thermal shock resistance and spalling resistance
Excellent ability of high refractoriness, anti-erosion of alkaline

                                                      magnesia refractory bricks for ladle working line

Application:

         As an excellent material ,can be used for magnesia bricks, unshaped refractory materials.

At same time can be used in metallurgy, building materials, chemical industry, national defense, scientific research, aerospace, medical equipment components and household appliances

products technical:

 

1.The products are fused magnesia as main raw material, after a reasonable size distribution, high pressure forming, high-temperature sintering. The product has strong resistance to slag corrosion ability and high temperature dimensional stability. Mainly used in glass furnace regenerator, the upper part.

 

2.The regular magnesia bricks are made from dense dead burned magnesia that makes the bricks in good refractoriness, corrosion-resistance, and widely used in checker chamber of glass tank, lime kiln, non-ferrous metallurgical furnaces, open heart furnace, iron mixer and EAF of steel-making, and also ferro-alloy furnace, etc.

 

The bricks with MgO 95% or more in content take the secondary-burning dead burned magnesia or electrofused magnesia as the raw material and bured under the condition of ultra high temperature. They have the features of highly directly bonded and corrosion-resistance and widely used in various kinds of high temperature kilns and furnaces

 

Magnesia Brick Features:

 

Excellent performance of basic slag resistance, high refractoriness, thermal stability, anti-erosion and anti-peeling

Excellent strength of pressure bending, abrasion proof

Excellent performance of high-temperature firing, high rates of associative property, anti-erosion ability

Excellent thermal shock resistance and spalling resistance

Excellent ability of high refractoriness, anti-erosion of alkaline residue;

High temperature load of refractoriness under load. High mechanical strength

High temperature resistance  Excellent corrosion resistance

Resistance to spalling

 

Item		Behaviors
		Fused Rebonding Magnesia Brick
		DMZ-95	DMZ-96	DMZ-97	DMZ-98
Chemical composition	MgO %	≥95	≥96	≥97	≥97.5
	SiO2 %	≤1.5	≤1.2	≤1.0	≤0.5
	CaO %	≤1.5	≤1.2	≤1.2	≤0.6
Apparent Porosity %		≤18	≤18	≤17	≤15
Cold Crushing Strength Mpa		≥55	≥60	≥60	≥60
0.2Mpa Refractoriness Under Load T0.6		≥1650	≥1680	≥1700	≥1700
Bulk Density g/cm3		≥2.95	≥3.0	≥3.05	≥3.05
Thermal Stability 950°C Wind cycles		≥15	≥20	≥20	≥20