offer high strength fireclay insulation refractory brick NG types of refractory bricks
Negotiable /Ton
Min.Order:2 Tons
Zhengzhou Sunrise Refractory Co., Ltd.
Fireclay Insulation types of refractory bricks
ISO 9001:2000 Certificate Manufacturer
We have exported to USA, India, Germany, Canada etc many countries, and they are satisfy with our products.
Fireclay Insulation types of refractory bricks are classified under temperature between 1300ºC and 1700ºC, manufactured from high purity alumina clay by mixing, press-forming, drying, sintering and machining. Bricks contain carefully-graded organic fillers which are burned out during sintering to give a uniform controllable pore structure. This technique makes product feature low thermal conductivity and excellent heat insulation
Fireclay Insulation types of refractory bricks can be used as a hot face lining directly exposed to the heat or as a backup insulation layer in iron and steel mills, non ferrous foundries, petrochemical, ceramic, glass, cement and oil fired electric power generating plants.
ADVANTAGES:
Light weight and low thermal conductivity allows thinner furnace walls
Maintain stable structural strength throughout ambient to maximum service temperature
Low heat storage results in rapid cooling and heating operation
Low iron and impurities to enhance reducing atmosphere
High thermal shock resistance in preventing spalling
Non standard sizes and shapes are available upon request
APPLICATIONS:
Ceramic shuttle kilns
Metal heat treatment furnaces Steel billet reheating furnaces Oil refinery heaters
Laboratory furnaces
Sunrise Brand | NG-0.5 | NG-0. 6 | NG-0. 8 | NG-1.0 | NG-1.3 | NG-1.5 | |
USA Brand | ISO125-0.5 | ISO125-0.6 | ISO135-0.8 | ISO135-1.0 | ISO140-1.2 | ISO140-1.5 | |
Max Service Temperature (°C) | 1150 | 1200 | 1280 | 1300 | 1350 | 1400 | |
Bulk Density (g/cm3) | 0.55 | 0.6 | 0.8 | 1.0 | 1.3 | 1.5 | |
Apparent Porosity % | 80 | 70 | 60 | 55 | 50 | 40 | |
Cold Crushing Strength (Mpa) ≥ | 1.5 | 2.0 | 2.5 | 3.0 | 4.0 | 6.0 | |
Reheating Linear Change (%) °CX 12H ≤ | 1250°C -0.5 | 1300°C -0.5 | 1350°C -0.5 | 1350°C -0.9 | 1350°C -0.9 | 1350°C -0.9 | |
Thermal conductivity(W/m.k) | 400°C | 0.14 | 0.25 | 0.35 | 0.41 | 0.51 | 0.6 |
600°C | 0.16 | 0.29 | 0.45 | 0.43 | 0.61 | 0.71 | |
800°C | 0.18 | 0.31 | 0.50 | 0.44 | 0.67 | 0.77 | |
1000°C | 0.20 | 0.33 | 0.60 | 0.45 | 0.8 | 0.9 | |
Al2O3 (%) | 37 | 40 | 40 | 40 | 40 | 42 | |
Fe2O3 (%) | 1.0 | 1.5 | 1.5 | 1.5 | 2 | 2 | |
SiO2 | 44 | 55 | 55 | 55 | 55 | 55 |