Specifications

low porosity fireclay bricks :
1.blast furnaces and hot blast furnaces;
2.waste incinerators and glass melting furnaces.

Clay bricks use Chamotte that the fire clay is calcinated as the main material. These bricks consist of fire clay and binder. The chemical components of these bricks are SiO2 and Al2O3.

 

 Applications

 

The main applications are the low temperature parts such as blast furnaces and hot blast furnaces, waste incinerators and glass melting furnaces. Due to the scale-up of a variety of industrial furnaces and severity of operating conditions, super dense clay bricks that made of more refined chamotte being calcinated at high temperature are applied more than before.

 

Description

Fire clay refractory brick with super-low thermal conductivity add foaming agent and stabilizing agent into the slurry confected by some refractory raw materials, such as alumina powder, refractory clay and cyanite. After mixing them, the refractory slurry evenly adsorbs around the foams, and spherical proes are formed after being dried and fired. The six faces are all cut by machine so that the sizes are accurate.

   

Main Properties

item	SK-32	SK-34	SK-36	SK-37	SK-38
AI2O3(%)	38	42	50	65	70
Fe2O3 (%)	3	2.5	2	2	0.3
Refractoriness (SK)	32	34	36	37	38
Refractoriness under load, 0.2MPa, Ta, ((°C)	1300	1350	1450	1550	1580
Porosity (%)	22-26	19-23	20-24	23	18
Bulk density (g/cm³)	2.05	2.1-2.15	2.3-2.4	2.5	2.62
Cold crushing strength (MPa)	25	25	45	45	51
Thermal expansion at 1000°C (%)	0.6	0.6	0.3	0.5-0.7	0.6