refractory material blast furnace fire clay brick
USD $300 - $500 /Ton
Min.Order:3 Tons
Zhengzhou Sunrise Refractory Co., Ltd.
refractory material fire bricks
Clay bricks use Chamotte that the fire clay is calcinated as the main material. These bricks consist of fire clay and binder. The chemical components of these bricks are SiO2 and Al2O3.
The main applications are the low temperature parts such as blast furnaces and hot blast furnaces, waste incinerators and glass melting furnaces. Due to the scale-up of a variety of industrial furnaces and severity of operating conditions, super dense clay bricks that made of more refined chamotte being calcinated at high temperature are applied more than before.
thickness (mm) | length (m) | ||
0.5 | 80 | ||
1.0 | 40 | ||
1.5 | 30 | ||
2.0 | 20 | ||
2.5 | 20 | ||
3.0 | 15 | ||
4.0 | 10 | ||
5.0 | 10 | ||
6.0 | 10 | ||
main performane | brand | ||
|
|
| |
classification temperature C | 1100 | 1260 | 1400 |
properties measured at ambient condition( 23C/50% RH ) |
|
|
|
meltig (minimum) C | 1760 | 1760 | 1760 |
bulk density ( minimum kg/m3) | >210 | 210 | 210 |
chemical composition % |
|
|
|
others % | - | 1 | <5 |
thickness | 0.5-6mm |
|
|
item | SK-32 | SK-34 | SK-36 | SK-37 | SK-38 |
AI2O3(%) | 38 | 42 | 50 | 65 | 70 |
Fe2O3 (%) | 3 | 2.5 | 2 | 2 | 0.3 |
Refractoriness (SK) | 32 | 34 | 36 | 37 | 38 |
Refractoriness under load, 0.2MPa, Ta, ((°C) | 1300 | 1350 | 1450 | 1550 | 1580 |
Porosity (%) | 22-26 | 19-23 | 20-24 | 23 | 18 |
Bulk density (g/cm³) | 2.05 | 2.1-2.15 | 2.3-2.4 | 2.5 | 2.62 |
Cold crushing strength (MPa) | 25 | 25 | 45 | 45 | 51 |
Thermal expansion at 1000°C (%) | 0.6 | 0.6 | 0.3 | 0.5-0.7 | 0.6 |