Properties 

Test Data

Unit

Density

0.91

g/cm3

Melt Index

0.8

g/10min

Rockwell hardness

70

R

Elongation at Break

500

%

Flexural modulus

1700

MPa

Tensile strength at yield

23

MPa

Vicat softening point

160

°C

Load the heat distortion temperature

110

°C