Specifications

Road making/polishing/blasting material--glass beads For Coating
1) Road reflecting mark
2) Used as disperser, grinding media

Road making/polishing/blasting material--glass beads For Coating

Glass beads

The glass beads are used for road marking paints and thermoplastic road marking material to provide

excellent night retro-reflectivity. 

Usually,the rate of glass beads in paint is 15%-25%. 

 

1.The specific gravity:2.4-2.6(g/cm3); 

2.Refractive index: not less than 1.5

3.Standard:JT/T446-2001;BS6088-1981; AASHTO M247;AS/NZS2009:2002 ; EN 1423:1997 and etc.

   can produce as client's requirements.

Glass beads

BS6088 CLASS A(PRE-MIX)
Diameter(um)	Retained(%)
>1180	0-3
1180-850	5-20
850-425	65-95
<425	0-10
Roundness:70% or better

 

 

BS6088 CLASS B(DROP-ON)
Diameter(um)	Retained(%)
>850	0-5
600-850	5-20
300-600	30-75
180-300	10-30
<180	0-10
Roundness:80% or better

 

Blasting glass beads
Items	Diameter(um)	Mesh Size
CYB-01	850-600	20-30
CYB-02	600-425	30-40
CYB-03	425-300	40-50
CYB-04	300-180	50-80
CYB-05	180-100	80-150
CYB-06	100-45	150-325

 

Grinding glass beads
Items	Diameter(mm)	Mesh Size
CYG-01	1.0-2.0	18-10
CYG-02	2.0-3.0	10-8
CYG-03	3.0-4.0	8-6
CYG-04	4.0-5.0	6-4

 

Road Line Markings Glass Beads

Reflective glass beads are made of  glass sand, after melting temperature the formation of a tiny glass beads, was observed under the microscope spherical, colorless, transparent, refractive index of 1.501.64 between the diameter is generally between 75 microns to 1400 microns. Currently in the domestic production of major road reflective glass beads craft flame floating method.
Reflective glass beads for road marking (paint) in the reflective material, can improve the retroreflective pavement marking paint performance, improve night driving safety, national transport sector has to be determined. When driving at night, the lights shone on road signs with glass beads online, make parallel light rays and reflected back, allowing the driver to see the way forward to improve the safety of driving at night. Now, reflective glass beads has become a road safety products, reflective material can not be replaced.
Reflective glass beads for road, mainly used in normal temperature, hot melt road marking paint, a method for premixed material can ensure marking period in the life of the long-term reflective; one kind of construction in the marking surface spreading, can play an instant reflection effect.
Coated glass beads are divided into two types, one as reflective highway A screen used as reflective. Coated glass beads is to use a high-performance organic materials on glass beads for external processing, making the glass bead surface adsorption air weakens the dust. As micro beads coated with a specific coupling agent, to improve the adhesion of the coating bead and to prevent deposition of micro beads to the paint. Because of its function floatability, the use in the coating surface float, which has the largest surface area can be increased more than 30% utilization. Glass bead coating processing performance is more superior. It rains more often foggy in humid environments, with better reflective capabilities.
Technical parameters
Appearance: colorless transparent sphere, rounded and smooth, no obvious bubbles or impurities.
Circularity: round rate of ≥ 80% Density :2.4-2 .6g/cm3 refractive index: Nd ≥ 1.50
Composition of: soda-lime glass composition, SiO2 content of> 70%
Some national standard:

 Chinese glass beads Standard: GB / T 24722 - 2009 No.1, 2, 3;

Korea glass beads Standard:  KSL 2521 No.1 and 2;
British glass beads Standard : BS6088 Class A and B;
American Standard:  AASHTO M247 type 1 and type 2;
European standard : EN1423 and EN1424;
Turkish Standard: TS EN1423;
New Zealand Standard:  NZS2009: 2002;
Taiwan Standard : CNS 

Japanese standard : JIS R3301;
Australian Standard Australian Standard : A, B, C, D.

  Glass beads

 

 

  Reflective glass bead for polishing/blasting material