Specifications

Sintered mullite
AL2O3: 70-77%min
Fe2O3: 0.1%max
SiO2: 22-29%
B.D.: 3.0g/cm3 min

Refractory Raw Material Sintered Mullite

Mullite is widely used as raw materials for high grade refractories:

such as the lining bricks in glass kiln furnace and bricks used in hot wind furnace in steel industry & Ceramic kiln and petrochemisty industry and many other applications.

 

Items		Unit	Index	Typical
Chemical composition	Al2O3	%	70.00-77.00	73.90
	SiO2	%	22.00-29.00	24.06
	Fe2O3	%	0.1 max(Fines 0.3%max)	0.08
	K2O+Na2O	%	0.40max	0.16
	CaO+MgO	%	0.4%max	0.08
Refractoriness		°C	1850min
Bulk density		g/cm3	3.00min	3.1
Glass phase content		%	5max
3Al2O3.2SiO2 Phase		%	95min