Specifications

Impact resistance,stripping resistance
Big tensile strength
Environmentally friendly products

In the experimental test which resistance to high oil temperature, It have shown that the use of this adhesive paste in the filter was soaked in oil (at high temperature of 135 °C or low temperature of -35 °C)for 192 hours, no shrinkage crack or degumming.

 

Technical parameters:

Two-component room temperature curing filter adhesive,    component proportion ratio is 6:1
Features	Material-A	Material-B
Physical nature	White Viscous liquid	Light yellow liquid
Color	Based on your request to configure
Bond strength	Initial bonding strength:20-21KN/CM2
	Peel strength:40-48KN/CM2
Working temperature	15°C-35°C
Viscosity:	30-45kps.s
Storage	3-6 months

 

 

 

 

 

 

 

 

 

 

 

 

Instructions:

1)      The surface of end cap is supposed to be washed clean for getting rid of oil stain and dust, and dried completely. Any oil stain, water or other impurities should not exist on the surface, or the adhesive strength will be affected.

2)      Before the charge mixture, material-A in the barrel should be stirred or inverted, material-A and material-B are mixed at the mixture ratio of 6:1 and stirred evenly.

3)      Inject appropriate adhesive into the end cap and wait for a moment. The adhesive should be smeared evenly on every corner of cap surface.

4)      Insert filter paper (or central tube) into the end cap and check the surfaces of two adhesive pieces. After complete contact, give a little pressure on the top of end cap and hold for a moment.

5)      After curing for around 2 hours, reverse and adhere the other end cap. It can be packaged when complete drying after 10 hours and used after 2 days.

 

bonding with metal cover and filter paper