Specifications

1.two component adhesive
2.room temperature
3.storage 9 months
4.environmentally friendly products
5.attend auto exhibition

Two-component room temperature curing filter adhesive, component proportion ratio is 6:1

Features:

1. Room temperature curing adhesive.

2. Anti-wear and oil resistance

3. Good adhesiveness for mental and paper

4. Impact resistance, stripping resistance, anti-vibration and anti-fatigue

5. Environmentally friendly products.

Physical Nature:

Appearance: material-A is white viscous liquid, and material-B is black liquid

Viscosity: 30-45kps.s 

Bond strength: Initial bonding strength :20-21KN/CM²

Peel strength:40-48KN/CM² 

Purpose: It is applicable for paper filter of such internal combustion engines as automobile and tractor, the cementation between paper and iron sheet or plastic.

Specifications of use:(usage) 

1. The surface of end cap is supposed to be washed clean for getting rid of oil stain and dust, and dried completely. Any oil stain, water or other impurities should not exist on the surface, or the adhesive strength will be affected.

2. Before the charge mixture, material-A in the barrel should be stirred or inverted, material-A and material-B are mixed at the mixture ratio of 6:1 and stirred evenly.

3. Inject appropriate adhesive into the end cap and wait for a moment. The adhesive should be smeared evenly on every corner of cap surface.

4. Insert filter paper (or central tube) into the end cap and check the surfaces of two adhesive pieces. After complete contact, give a little pressure on the top of end cap and hold for a moment.

5. After curing for around four hours, reverse and adhere the other end cap. It can be packaged when complete drying after 24 hours and used after five days.

Package: plastic barrels and plastic pots

Two-component room temperature curing filter adhesive, component proportion ratio is 6:1
Features	Material-A	Material-B
Physical nature	White Viscous liquid	Black liquid
Color	Based on your request to configure
weight	30kg	5kg
package	Plastic bucket or tin bucket	Plastic pots
Bond strength	Initial bonding strength:20-21KN/CM2
	Peel strength:40-48KN/CM2
Working temperature	15°C-35°C
Viscosity:	30-45kps.s
Storage	3-6 months

 

 

 

 

 

 

 

 

 

 

 

 

 

In the experimental test which resistance to high oil temperature, It have shown that the use of this adhesive paste in the filter was soaked in oil (at high temperature of 135 °C or low temperature of -35 °C)for 192 hours, no shrinkage crack or degumming.