As fabricated (no mechanical property limits specified).

Annealed - products achieving the required annealed properties after hot forming 

processes may be designated as O temper.

Slightly strain-hardened from working at an elevated temperature from a limited 

amount of cold work (mechanical property limits specified).

Solution heat-treated, cold worked and naturally aged.

Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5% 

to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold-finished rod and

bar, 1% to 5% for hand or ring forging and rolled ring)and naturally aged. The products

receive no further straightening after stretching.

Solution heat-treated and naturally aged.

Cooled from an elavated temperature shaping process and then artificially aged.

Solution heat-treated and then artificially aged.

Solution heat-treated, stress-relieved by controlled stretching (permanent set 0.5%

to 3% for sheet, 1.5% to 3% for plate, 1% to 3% for rolled or cold finished rod and

bar, 1% to 5% for hand or ring forging and rolled ring) and then artificially aged.