Product Details

Specifications

Rigid UL PVC Compound
1.70C Jacket Grade PVC compound
2. Perfect plasticization,symmetrical color,without obvious impurities

Rigid UL PVC Compound

and Application

Material Name	Model	Application and Cable Criterion
70 PVC Jacket Material	H-70	For making 450/750V or lower voltage cable jacket, comply with GB/T8815-2002 and ROHS
70 Flexible PVC Jacket Material	HR-70	For making 450/750V or lower voltage cable jacket, comply with GB/T8815-2002 and ROHS
90 PVC Jacket Material	HI-90	For making 35KV or lower voltage cable jacket, comply with GB/T8815-2002 and ROHS

Instruction

This compound material is mainly made of PVC resin, by adding plasticizers, stabilizers, pigments and other additives.

Size: 4mm×3mm cylinder

Color: Black, White and Gray, special color can be made according to customers requirement.

Features

Test Item	Standard Value
Test Item	H-70	HR-70	HI-90
Tensile strength(Mpa)	≥15.0	≥12.5	≥16.0
Elongation (%)	≥180	≥200	≥180
Strike brittle temperature()	-25	-30	-20
Volume resistivity at 20(Ω.m)	1.0×10⁸	1.0×10⁸	1.0×10⁹
Dielectric strength (mv/m)	≥18	≥18	≥18
Heat distortion (%)	≤50	≤65	≤40
Heat stableness at 200 (Minute)	≥50	≥60	≥80
Heat aging
Heat aging temperature ()	100±2	100±2	100±2
Heat aging time (h)	168	168	240
Tensile strength after aging (Mpa)	≥15.0	≥12.5	≥16.0
Tensile strength change (%)	±20	±20	±20
Elongation after aging (%)	≥180	≥200	≥180
Elongation change (%)	±20	±20	±20
Weight loss g/m²	≤23	≤25	≤15

Packing and Store: packing by plastic bag, 25KGS/bag; store in dry ventilated warehouse, avoiding sunshine and rain.

Remark: the rigidity, density, color of the material can be adjusted according to customers requirement.