Forged Hot Work Mould Steel 1.2344/ H13/ SKD61 round bar
USD $2,416 - $2,658 /Ton
Min.Order:1 Ton
Dongguan City Yaoteng Special Steel Co., Ltd.
Quality and Quantity Assured 1.2344/ H13/ SKD61/4Cr5MoSiV1 Forged Hot Work Mould Steel
| |||||||||||||||
1.ChemicalComposition(%) |
| ||||||||||||||
| |||||||||||||||
2.Equivalent Grades |
H13/1.2344/SKD61 | ||||||||||||||
3.Form&Size | 1)Dongguan Yaoteng Special Steel Company are manufacturers and suppliers of SKD61 Tool Steel round bars, flat/square bars,plates,sheets. | ||||||||||||||
2)SKD61 Tool Steel Size Available(Length can be customized):
| |||||||||||||||
4 Round bar |
Round steel bar 10-800mm
| ||||||||||||||
5.Flat bar |
Flat steel bar 6-400mm*200-1600mm
| ||||||||||||||
6.Surface Condition | H13(1.2344/SKD61), EFS H13(8407), 1.2714(SKT4/5CrNiMoV)
| ||||||||||||||
7. Characteristic |
pure steel vacuum degassing refining process ball the annealing softening treatment, good cutting performance. SKD61 picture
strengthening elements vanadium, molybdenum special Add, abrasion resistance is extremely excellent | ||||||||||||||
8. Usage |
SKD61 a high-carbon high-chromium alloy tool steel with high hardness and wear resistance after heat treatment and hardenability, good dimensional stability, suitable for making high-precision long-life cold work die and thermosetting molding plastic mold. | ||||||||||||||
9. Physical properties
10.heat treatment
11. Cryogenic treatment | SKD61 Hardness: before heat treatment SKD61 about HRC15 ~ 20 (HB200 230), the hardness after heat treatment: the internal of HRC40 ° ~~ 45 ° surface HV1000 ± 100 SKD61 density is 7.85 g per cubic centimeter
| ||||||||||||||
Quenching: the first stage of warm-up: the second stage of 500 to 550 ° C Preheat: 750 ~ 800 °C quenching or high-pressure gas cooling, 100 ~ 150 °C into the back to the stove. Tempering: Preheat: 300 to 350 °C tempering heating: 550 to 680 °C air cooling to room temperature, tempering three times. Quenching temperature of 1020 to 1050 degrees, hardness 56 ~ 58HRC, heat treatment of small deformation, surface nitriding nitriding processing products have better wear resistance. | |||||||||||||||
In order to obtain the highest hardness and dimensional stability, the mold immediately after the quenching cryogenic -70 to -80 ° C., maintained for 3-4 hours, and then in the tempering treatment, the cryogenic treatment of tool or mold hardness than the hardness of conventional heat treatment 1 -3HRC. Complex shape and size changes in large parts, cryogenic processing production risk of cracking | |||||||||||||||
10.QualityCertificate | 1)Grade,Size,Quantity in Number & Weight
|
SEE MORE PRODUCT
contact us
Sales Merchandiser:Winnie
Telephone: 86-0769-33899333
E-mail: winnie AT toolsteel DOT net DOT cn
winnie AT otaisteel DOT com
Skype:928469037
TM:cn1018125490
W: http://toolsteel.en.china.cn
Company Address: 3 fang,xiansha,Gaobu town,Dongguan City,Yaoteng Trade Co., Ltd.