Specifications

PVC Coated Fabric for Truck Cover
anti-UV & anti-oxidation
high-temperature & cold resistance
waterproof & anti-pollution

 PVC Coated Tarpaulin Material

 

The material comprises a stable woven polyester fabric coated on both sides with PVC. Weave density and material, combined with the quantity of PVC, determine the quality and strength of the finished tarpaulin.

 

Hai Ben PVC Coated Tarpaulin is produced by digital control coating machine which composited PVC paste on polyester fiber substrate by roller coating, then it is heated by temperature regulating device and pressed on the tarpaulin accurately, cooling to be finished product afterward.

 

 

Features:

 

1. Excellent waterproof performance, anti-permeable ≥20KPa.

2. Obvious mildew proofing and inflame-retarding properties, flame retardant ≤ 10 seconds.

3. Anticorrosion including: acid, alkali and brine corrosion, and etc.

4. Heat resistance, and be able to adapt to variety of open-air natural conditions.

5. Good low-temperature flexibility, this fabric will not be fractured by pliers at -30°C.

6. Almost nonabsorbable of water, drying quickly after the rain without adding weight, convenient in usage.

7. Heat combined with high-frequency, which guaranteed this fabric water tight and will not crack.

8. High strength of tensile.

 

 

Technical Indexes:

 

 

Base Fabric	Total Weight (G/sqm)	Tear Strength (N/5cm)	Tensile Strength (N/5cm)	Peeling Strength (N/5cm)	Temperature Scope (°C)
500D*500D	440G	240*240	1800/1600	>30	-20~70'
18*12/inch
500D*500D	550G	260*320	760*780	>60	-20~70
9*9/inch
1000D*1000D	650G	180*160	1500/1500	>60	-20~70
9*9/inch
1000D*1000D	650G	360*395	760*780	>60	-20~70
20*20/inch
1000D*1000D	680G	360*410	2800/2600	>60	-20~70
20*20/inch