Titanium and Titanium Alloy Processing Wood for Implants for Surgery
USD $20 - $40 /Kilogram
Min.Order:1 Kilogram
Baoji Qixin Titanium Co., Ltd.
1.Application
Medical equipment , medical equipment , dental implants
2.High quality
Bar silk material transverse low power without cracks, porosity, metal or nonmetal inclusion and other visible defects
3.Feature
Designation no | Shape | Condition | Standard(mm) |
Gr1 Gr2 Gr3 | panel | (R.M) | thickness4.1~10.0 |
(Y.M) | thickness0.8~4.0 | ||
bar | (R.M) | Diameter8~75 | |
silk | (M) | Diameter0.6~6 |
4.Chemical composition
Designation no | Chemical Composition % | |||||||||
Bases | Impurity element ≤ | Others ≤ | ||||||||
Ti | AL | V | Fe | C | N | H | O | Each | Total | |
Gr1 | __ | __ | __ | 0.25 | 0.10 | 0.03 | 0.01 | 0.20 | 0.1 | 0.4 |
Gr2 | __ | __ | __ | 0.30 | 0.10 | 0.05 | 0.01 | 0.25 | 0.1 | 0.4 |
Gr3 | __ | __ | __ | 0.40 | 0.10 | 0.05 | 0.01 | 0.30 | 0.1 | 0.4 |
5.Board room temperature mechanics, process performance
Designation no | Standard | Tensile Strength ó b(Mpa) | Yield Strength ó 0.2(Mpa) | Elongation δ(%) | Bend Degree |
≥ | |||||
Gr1 | 0.8~5 | 370 | 250 | 20 | 130 |
>5~10 | 370 | 250 | 20 | __ | |
Gr2 | 0.8~5 | 440 | 320 | 18 | 100 |
>5~10 | 440 | 320 | 18 | __ | |
Gr3 | 0.8~2 | 540 | 410 | 15 | 90 |
>2~5 | 540 | 410 | 15 | 80 | |
>5~10 | 540 | 410 | 15 | __ |
6.Bar room temperature mechanical properties
Designation no | Standard | Tensile Strength ó b(Mpa) | Yield Strength ó 0.2(Mpa) | Elongation δ(%) | Reduction of area Ψ(%) |
≥ | |||||
Gr1 | 8~75 | 370 | 250 | 20 | 30 |
Gr2 | 8~75 | 440 | 320 | 18 | 30 |
Gr2 | 8~75 | 540 | 410 | 15 | 28 |