Hot dipped galvanized steel coils are produced by immersing steel in a zinc bath. 

An appropriate galvanizing process requires a pretreatment process during which the steel passes 

through different baths which prepare the surface for zinc coating. 

In this stage, chemicals are used to clean the surface of the steel. After the chemical treatment, 

the steel coils pass through a bath of melted zinc at temperatures around 460 ° C. The resulting uniform 

coating is finished through a process of skin-passing to provide smooth and shiny

appearance of the finished product. 

To store for a longer period, the hotdip galvanized coils can be delivered with a final oil coating, 

according to the customer’s demand.

PROFILAND STEEL produces hot-dip galvanized steel coils with very good workability

 at further cold forming and bending processes.

Technical specification for the hotdip galvanized :

• Steel grade: DX51D+Z

• Zinc coverage: 30-180 g/sqm on both sides (depending by the requested specification);

• Thickness: between 0,2 mm and 1,00 mm;

• Width: 600mm,914mm,1000mm, 1220mm and 1250 mm;• Coil weight: 4-6 mt;

• Coil ID: 508 mm;

• Coil OD: 900-1500 mm ;

Depending on their usage, the hot-dip galvanized coil can be delivered slightly oiled.

The detailed information:

Technical data of hot dipped galvanized coil