Monel K500(UNS N05500)
Alloy K-500 is a nickel-copper alloy, precipitation hardenable through additions of aluminum and titanium. This alloy retains the excellent corrosion resistant characteristics of 400 and has enhanced strength and hardness after precipitation hardening when compared with 400. Alloy K-500 has approximately three (3) times the yield strength and double the tensile strength when compared with 400. K-500 can be further strengthened by cold working before the precipitation hardening.
Typical applications for alloy K-500 are pump shafts and impellers; doctor blades and scrapers; oil-well drill collars and instruments; electronic components; springs; and valve trim.
Material:Monel K500
Size: OD Φ 1m~120mm; WT: 0.1mm~10mm
Exported country: Italy, Argentina, Spain, Canada, Australia.
Typical analysis in percent
C | MN | S | Si | Ni | Al | Fe | Ti | Cu |
0.18max | 1.5 max | 0.01 max | 0.50 max | 63.0 min | 2.30-3.15 | 2.0 max | 0.35-0.85 | 27.0-33.0 |
Physical properties
Density:8.44g/cm3
Melting range:1315-1350°C
Typical mechanical properties(At room temperature)
Ultimate tensile strength(MPa) | Yield strength(MPa) | Elongation in 50 mm(%) |
965 | 690 | 20 |