Specification:
| Properties | Unit | Test method | Value |
| Melt Flow Rate | |||
| Melt flow rate(230°C/2.16KG) | g/10min | ISO 1133 | 12 |
| Mechnical Properties | |||
| Tensile modulus of elasticity(v=1mm/min) | Mpa | ISO 527-2 | 1550 |
| Tensile yield at stress(v=50mm/min) | Mpa | ISO 527-2 | 35 |
| Tensile yield at strain (v=50mm/min) | % | ISO527-2 | 8 |
| Tensile strain at break (v=50mm/min) | % | ISO 527-2 | >50 |
| Charpy impact strength unnotched(+23°C) | KJ/m2 | ISO 179/1eU | 110 |
| Charpy impact strength notched(+23°C) | KJ/m2 | ISO 179/1eU | 3.0 |
| Izod Impact strength notenched(+23°C) | KJ/m2 | ISO 180/1A | 3 |
| Ball indentation hardness(H 358/30) | Mpa | ISO 2039-1 | 78 |
| Thermal Properties | |||
| Melting point,DSC | °C | ISO 3146 | 163 |
| Heat deflection temperature ------------HDT/B(0.45Mpa) | °C | ISO 75-2 | 85 |
| Vicat softening temperature ------------VST/A50(10N) | °C | ISO 306 | 154 |
| Other Properties | |||
| Density | g/cm3 | ISO 1183 | 0.91 |