Properties

Unit

Test method

Value

Melt Flow Rate

Melt flow rate(230°C/2.16KG)

g/10min

ISO 1133

12

Mechnical Properties

Tensile modulus of elasticity(v=1mm/min)

Mpa

ISO 527-2

1550

Tensile yield at stress(v=50mm/min)

Mpa

ISO 527-2

35

Tensile yield at strain (v=50mm/min)

%

ISO 527-2

8

Tensile strain at break (v=50mm/min)

%

ISO 527-2

>50

Charpy impact strength unnotched(+23°C)

kJ/m2

ISO 179/1eU

110

Charpy impact strength notched(+23°C)

kJ/m2

ISO 179/1eA

3.0

Izod Impact strength notenched(+23°C)

kJ/m2

ISO 180/1A

3

Ball indentation hardness(H 358/30)

Mpa

ISO 2039-1

78

Tests

Value

Unit

Melt Flow Rate

45

g/10min

Density

0.90

G/cm3

Elongation Stress 

10

%

Flexural modulus

14

Mpa

Rockwell hardness

95

R scale

IZOD impact strength

6.5

kg.cm/cm

Vicat softening point

152

°C

Heat distortion temperature

125

°C