Specifications

Used in urea prilling tower wall protective coating, also used for concrete, metal material anti-corrosion coating.

Composition

1 Toluene diisocyanate is the main material.

2 The other is epoxy resin liquid

3 The last is catalyst

Ratio (weight ratio) for:

Ingredient 1: 2:3 = 100:10:0.35

 

Characteristics

Good physical and mechanical properties and excellent anti-corrosive

 

Usage:

Use together with H06-2 Iron oxide red ,brownish yellow Polyurethane primer and S04-4 grey  Polyurethane enamel,S07-1 black Polyurethane putty as in urea prilling tower wall protective coating, also used for concrete, metal material anti-corrosion coating.

 

Specification

Items		Standards
Appearence		Yellow or light brown yellow transparent liquid
Content of solid material		67-73%
Dry time,H,No more than	Surface Dry	2 hours
	Inner dry	20 hours
Flexibility,mm		1
Impact strengh,kg/sq.cm  No less than		50
Hardness  No less than		0.6
Adhesion   No less than		1

 

Construction reference

1 Coordinate the three as the ratio requirements. Used all the coordinated paints in 6 hours.

2 Keep all the tools dry and clean.The coated object surface must be clean, dry, no acid and alkaline, bright and clean.

3 Thinner can use anhydrous Cyclohexanone and anhydrous Xylene (ratio :1 : 1). 

  Do not use alcoholic solvents.