Product Details

Brief introduction for powder coating
It is a thermosetting type of powder coating made of polyester resin,colors,fillers and agents. It has excellent mechanical property and terrific leveling property and applies to any indoor metal equipment such as home appliance,office furniture,lighting apparatus equipment,sports equipment etc.

Powder property
Specific gravity 1.21.8g/cm³,(different according to formulas and colors)
Partical size distribution: 100% less than 100 mmm(adjust according to different uses)
Curing conditions:
normally curing: At 180 for 15 minutes(temperature of workpieces)
at 200 for 10 minutes (temperature of workpieces)

property of coating films

Testing items	testing standard	testing quotas
Gloss	GB/T9754-1988 60°angle	high gloss≥86%,plain gloss 15-69%,glossless 0-15%
pencial hardness	GB/T6739-1996	2H
adhensive force	GB/T9286-1988	0 grade
bend	GB/T6742-1986	Φ3 axis without cracks
impact resistance	GB/T1732-1993	50kg/cm
salt spray fog test	GB/T1771-1991	400 hours
sticky test	GB/T1740-1979	1000 hours
notes:1.The above tests use cool rolled steel plates of 0.8mm thick , without oils and zinc phophorization ,with coating films of 5070µm. 2.The property quotas of the above coating film may drop with the declining of the gloss'

package,storage and transport

Packed in paper box with polyvinyl inside bag, Net.W 15kg or 20kg per box,the products should be stored in rooms well-ventilated,cool,dry and clean with a temperature below 30.They should not be put in the sun or in the open air .Organic solvent,oil,water and other things should be avoided mixing Stored in the above conditions,all the products can keep efficient for one year;The products beyond the storage time can be rechecked ,if still effective ,they still can be used.

sanitation and protection

Although the powder coating is non-toxic, protection still should be paid attention to to keep the powder from entering eyes or being absorbed. Opeators should wear antisepic gauze and preventive clothing to prevent the skin from contacting the coating over a long period of time.