Name: fire rated 1000 Calcium Silicate Board for thermal insulation
Brand: DKJL
Availability: InStock

Product Details

fire rated 1000 Calcium Silicate Board for thermal insulation

Product Description

High density calcium silicate insulation board is developed for nonferrous metal industry with density range 800-1000KGS/M3, used for conveying, casting and molding of molten alumina and other non-ferrous metals, also can be used as clamping fixture in glass industry. Besides its own thermal insulation, its non-stick aluminum characteristics have been greatly played. High strength, good machinability, can be used to machine precision products and complex parts by Numerical Control Machine Tools.

There are two types of board reinforced by glass fiber and carbon fiber.

Features and advantage

1. Low thermal conductivity and less heat lost in high temperature

2. Not wetted by molten alumina

3. Resistance to thermal shock

4. Excellent machining performance

5. Asbestos-free

Application

1. Ladle insulating panels

2. Clamping fixture for car glass

3. Dip tubes

4. Pouring spouts

5. Hot-top rings

6. Stopper pins

7. Rolling edge

8. Floats

9. Launders

1000 calcium silicate board for ducting Technical index

Item	DK-800	DK-801
Type	Glass fiber reinforced	carbon fiber reinforced
bulk density kg/m3	850-950 kg/m3	850-950 kg/m3
temp limit °C	1000-1100 °C	1000-1100 °C
continuous service temp °C	850°C	850°C
flexural strength MPa	6.5	8
compressive strength(break)5%deformation	15.5 MPa 12MPa	17 MPa 13 MPa
coefficient of thermal expansion/°C	7*10-6	7*10-6
thermal conductivity (W/M.K)	100°C 200°C 300°C 400°C 0.113 0.120 0.121 0.125	100°C 200°C 300°C 400°C 0.103 0.114 0.124 0.133
thermal shrinkage% after 24 hours lineal % Thickness %	650°C 700°C 750°C 850°C 1000°C 0.15 0.25 0.28 0.35 0.49 0.86 1.00 1.10 1.30 3.50	650°C 700°C 750°C 850°C 1000°C 0.10 0.18 0.20 0.21 0.36 0.60 0.80 0.90 1.10 2.40