Features:

1) High quality aluminum base with electrolytic graining and anodizing treatment

2) The surface grained plate could shorten the draw-down time and halo formation during exposure3) Easy to distinguish the visual contrast between the exposed region and non-exposed region after processing4) Suitable for machine, manual and tank processing5) High impression rabilityOuter packing:50pcs/pack

 
PS PLATE TECH SHEET
Long run ps-plate, positive working subtractive, electrochemical grained and anodized on aluminum base of
99.5 alloy AA 1050.
 

EXPOSURE
Metal halide UV light source is recommended, with 5000Watt light and distance of 100-120cm, the timing 10-
12 seconds to obtain perfect image reproduction and UGRA or Stouffer Scale/grey
scale step 3-4 clear and 10-12 micron lines broken away.
 
DEVELOPMENT
Developer conductivity min. 70mSmax 110ms, temperature 20-24 Celsius, developer contact time 15-20
seconds. Developer DCTP-2000 at 85mS, 24 Cels. 20 seconds contact time, compatibel with most popular
positive developers.
 
 
Storage
It is recomended in the yellow light ,Should avoid of direct sunlight . Stored in dry ,cool,ventilated place ,Tempreature preferably 18-28°C,Humidity below 65%.
Keep away from chemicals.

PHYSICAL & DIMENSIONAL STRUCTURE:
Roughness (Ra) min. 0.55um - 75um
Anodic layer 3.0gr/sqmeter
Nominal thickness: 015 - 0.25 - 0.30 mm
TOLERANCES
For thickness: 0.15 / 0.20mm +/- .010mm - .015mm
0.25 / 0.30mm +/- .010mm - .025mm

Flatness
Surface waves as per DIN 1784 max. 0.75%

Packing
Plates are wrapped in photo protective paper and packed in carton boxes. The weight of boxes is vary according to
size and thickness.
for 0.15mm is 100 pieces plates each carton 
for 0.20mm  is  50  pieces plates each carton 
for 0.25mm is  50 pieces plates  each carton
for 0.30mm 50 pieces plates, large sizes depends on sizes