Specifications

calcium silicate board panel
It is made from wood lengthy fiber, concrete and silicon sand, under the high pressure water va

Calcium Silicate Board is mainly made of siliceous and calcareous materials as major  and natural cellulose reinforced, forming in Hatschek process and high pressure (4000 tons and fumigation(in autoclave for 24 hours),Which has the advantages of high strength, light weight, anti- freeze, water-resist, fire-proof, damp-proof, sound-absorption , no distortion and no radiation...Etc. Used as suspended ceiling, partition, heat insulating board, base plate, external wall panel, exterior wall cladding, paneling, flooring, back-liners, skirting lines, prefabricated structures, door shutters …etc.  

 

Applications: Business building, Entertainment facility, supermarket, hotel & restaurant, factory, warehouse, apartment building, hospital, theater and station etc. 

 

Materials: Tobermorite, CaO, Quartz sand, cellulose fiber

Fire-proof rate: A-class incombustible (GB8624-1997)

Incombustibility: 180 minutes (GB/T9978-1999)

Density: 1.1-1.5g/cm3

Moisture: <10%

Heat conduction: 0.24W/MK (Jc/t564) Average 

Sound-absorption: 45db (GBJ75-84)

Anti-bend strength: >15MPa (GB/T7019-1997)

Moisture movement rate: <0.19% (GB/T7019-1997)

Dry shrinking rate: <0.09% (GB/T7019-1997)

Radiation rate: According with Standard (GB6566-2000)

Product Name	Calcium silicate board	Gypsum Board	Fiber Cement board
materials	siliceous material, lime fractory and reforcing fiber	Gypsum power ,paper ,reforcing fiber	Cement, natural fiber reinforced
Flexural strength (Mpa)	>12  (6mm calcium silicate strength = 12mm gypsum board strength)	4-5	>16
Fireproofing features	Incombustible A-class material (GB8624-1997)	difficult-flammability	Incombustible A-class material (GB8624-1997)
Refractory High-point	>240min	60min	>240min
Moisture proof features	After wetting,the strength drops by 20-40%,recovers to 100% after dryness	Distortion after wetting,beyond retrieve	After wetting,the strength drops by 20-40%,recovers to 100% after dryness
Service life	Used for many years	Sagging because of absorbing the moisture in the air,short lifetime	Used for many years