Fine apparent density low oxygen content metal powders for 3d printing
Specification
With the development of science and technology, 3d rapid prototyping improves dramatically. AlSi10Mg, TC4, 316L as well as other metal powders are in great demand.
Parameters for AlSi10Mg:
Chemical components |
Al | (balance) |
Si | (9.0 – 11.0 wt-%) | |
Fe | (≤0.55 wt-%) | |
Cu | (≤0.05 wt-%) | |
Mn | (≤0.45 wt-%) | |
Mg | (0.02 - 0.45 wt-%) | |
Ni | (≤0.05 wt-%) | |
Zn | (≤0.05 wt-%) | |
Ti | (≤0.15 wt-%) | |
P, S | (each≤0.01 wt-%) | |
Density | 2.67g/cm³ | |
Particle size | -250mesh | |
Powder particle specific surface area | 0.3250m/g | |
Degree of sphericity | ≥95% | |
Recommended layer thickness | 30, 40 um | |
Apparant density | 59.3% | |
Relative density of formed part | approx. 100% |
Competitive advantage
We adopt our mature and advanced vacuum gas atomization equipment for the mass production of the metal powders.
Oxygen content can be controlled to about 700-800ppm.
The shape of the powder is spherical with less satellite.
High errosion resistance property.
Optimal heat resistance property.
Fine mechanical property.
The powders can be widely used in 3d printing and laser cladding for industrial spare parts, areospace spare parts, instrument spare parts, as well as gas turbine spare parts.
Detailed image
Advanced and mature vacuum gas atomization technology.