Specifications
1.Professional manufacture, many years in thsi line2.adsoprtion for water, CO2,SO2 and others
3. Molecular: 3A.4A.5A.13X
Moelcualr Sieve Type:3A.4a.5a.13x
Technical Parameter for 3A Molecular Sieve
Item | Unit | Technical data | |||
Shape |
| Pellet | Sphere | ||
Diameter | mm | 1.5-1.7 | 3.0-3.3 | 1.7-2.5 | 3.0-5.0 |
Size ratio up to grade | % | ≥98 | ≥98 | ≥96 | ≥96 |
Bulk density | g/ml | ≥0.64 | ≥0.64 | ≥0.68 | ≥0.68 |
Wear ratio | % | ≤0.20 | ≤0.25 | ≤0.10 | ≤0.10 |
Crushing strength | N | ≥45/cm | ≥60/cm | ≥30/piece | ≥70/piece |
Static water adsorption | % | ≥20 | ≥20 | ≥20 | ≥20 |
Ethylene adsorption | % | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 |
Water content, as shipped | % | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Technical Parameter for 4A Molecular Sieve
Item | Unit | Technical data | |||
Shape |
| Pellet | Sphere | ||
Diameter | mm | 1.5-1.7 | 3.0-3.3 | 1.7-2.5 | 3.0-5.0 |
Size ratio up to grade | % | ≥98 | ≥98 | ≥96 | ≥96 |
Bulk density | g/ml | ≥0.66 | ≥0.66 | ≥0.66 | ≥0.66 |
Wear ratio | % | ≤0.20 | ≤0.40 | ≤0.20 | ≤0.20 |
Crushing strength | N | ≥30/cm | ≥45/cm | ≥30/piece | ≥70/piece |
Static water adsorption | % | ≥20.5 | ≥20.5 | ≥21 | ≥21 |
Static methanol adsorption | % | ≥15 | ≥15 | ≥15 | ≥15 |
Water content, as shipped | % | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Technical Parameter for 5A Molecular Sieve
Item | Unit | Technical data | |||
Shape |
| Pellet | Sphere | ||
Diameter | mm | 1.5-1.7 | 3.0-3.3 | 1.7-2.5 | 3.0-5.0 |
Size ratio up to grade | % | ≥98 | ≥98 | ≥96 | ≥96 |
Bulk density | g/ml | ≥0.61 | ≥0.61 | ≥0.64 | ≥0.64 |
Wear ratio | % | ≤0.10 | ≤0.20 | ≤0.10 | ≤0.10 |
Crushing strength | N | ≥30/cm | ≥45/cm | ≥25/piece | ≥65/piece |
Static water adsorption | % | ≥23.5 | ≥23.5 | ≥23.5 | ≥23.5 |
Static CO2 adsorption | % | ≥18 | ≥18 | ≥18 | ≥18 |
Water content, as shipped | % | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Technical Parameter for 13X Molecular Sieve
Item | Unit | Technical data | |||
Shape |
| Pellet | Sphere | ||
Diameter | mm | 1.5-1.7 | 3.0-3.3 | 1.7-2.5 | 3.0-5.0 |
Size ratio up to grade | % | ≥98 | ≥98 | ≥96 | ≥96 |
Bulk density | g/ml | ≥0.61 | ≥0.61 | ≥0.64 | ≥0.64 |
Wear ratio | % | ≤0.10 | ≤0.20 | ≤0.10 | ≤0.10 |
Crushing strength | N | ≥30/cm | ≥45/cm | ≥25/piece | ≥65/piece |
Static water adsorption | % | ≥23.5 | ≥23.5 | ≥23.5 | ≥23.5 |
Static CO2 adsorption | % | ≥18 | ≥18 | ≥18 | ≥18 |
Water content, as shipped | % | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |