1>Chemical requirements
Grade | N | C | H | Fe | O | Al | V | Pa | Mo | Ni | Ti |
1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18 | / | / | / | / | / | bal |
2 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | / | / | bal |
3 | 0.05 | 0.08 | 0.015 | 0.30 | 0.35 | / | / | / | / | / | bal |
4 | 0.05 | 0.08 | 0.015 | 0.50 | 0.40 | / | / | / | / | / | bal |
5 | 0.05 | 0.08 | 0.015 | 0.40 | 0.20 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
7 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
9 | 0.03 | 0.08 | 0.015 | 0.25 | 0.15 | 2.5~3.5 | 2.0~3.0 | / | / | / | bal |
12 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |
2>Product details
Titanium Wire | |
Material | Pure Titanium and Alloy Titanium |
Grade |
|
Standard | ASTM B863 |
Specification | Dia0.1-Dia7.0mm |
Surface Treatment | Polishing,Pickling |
Supply Form |
|
Applications |
|
3> Tensile requirements
Material | Specifications(mm) | State | Room-temperature Mechanical properties, ≥,% | |||
σb Mpa(ksi) | σ0.2 Mpa(ksi) | δ % | Ψ % | |||
Gr1 | 3.2-6.35 | Annealing(M) | 240 | 170 | 24 | 30 |
Gr2 | 345 | 275 | 20 | 30 | ||
Gr3 | 450 | 380 | 18 | 30 | ||
Gr4 | 550 | 483 | 15 | 25 | ||
Gr1 | 1.6-3.2 | 240 | 170 | 15 | --- | |
Gr2 | 345 | 275 | 12 | --- | ||
Gr3 | 450 | 330 | 10 | --- | ||
Gr4 | 550 | 483 | 8 | --- | ||
Gr1 | 1.0-1.6 | 240 | --- | 12 | --- | |
Gr2 | 345 | --- | 10 | --- | ||
Gr3 | 450 | --- | 8 | --- | ||
Gr4 | 550 | --- | 6 | --- | ||
4> Advantage
1.Baoji Qixin Titanium Co,. Ltd is located in "The Chinese Titanium Valley" who has specialized in Titanium Anode and Titanium Material for 10 yeas old.
2.Technical Standard
Final product test: Ultrasonic test, Eddy current test, Hydraulic test, Flaring test and so on.
3.Certification: ISO9001, SGS, PED.
4. Production capacity:150 tons/ per year.
5.BEST SEVICE:Can be customized and shipment quickly .
6. First quality and competitive price .
5>Product display
Detailed information on www.qixinti.com . If you have any need,pls contact us. Looking forward to WIN-WIN cooperation .