Low Cr Alloy Steel Mill Liners For Conch Cement Group With More than HRc50
Negotiable /Piece
Min.Order:1 Piece
Wuxi Orient Anti-wear Engineering Company
Steel Cr-Mo Wear Alloy Steel Castings Liners For Conch Cement Mill
High Manganese Steel Casting Ball Mill Liners Less Than HB300 For Cement Mill
HRC52 High Cr White Iron Castings End Liners For Cement Mill Iron Casting
Cr12 Iron High Cr Iron Castings Cement Mill Liners , Shell Liners DF022
High Iron Cr Cement Mill Liners For High Abrasion Performance
1. Low Cr Alloy Steel Liners are designed for high impact value & abrasion performance.
2. More than HRC50, more than AK49J.
Low Cr Alloy Steel Liners for Conch Cement Mill Description:
1. Hardness difference from surface to center is less than HRc2.
2. Low Cr Alloy Steel Liners are designed for high impact value & high abrasion performance.
3. More than HRc50, AK49-88J.
In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0.10~1.00 |
0.10~1.00 |
- |
- |
Ni |
≤0.50 |
≤0.30 |
0~0.30 |
0~0.30 |
0~0.30 |