Items | Content | ||
Submerged nozzle | Ladle nozzle | ||
SiO2 ≥% | 99.1 | 99.2 | |
ZrO2 ≥% | 75 | 75 | |
C ≥% | 10 | 10 | |
SiC ≥% | 5 | 5 | |
Al2O3 ≥% | 65 | 65 | |
A.P. %≤ | 14 | 15 | |
C.C.S. Mpa≥ | 46 | 45 | |
B.D. g/cm3≥ | 1.90 | 1.90 | |
Thermal shock≥ | 30 | 30 |
Place of Origin | Henan, China |
Shape | Pipe |
Material | Other |
SiO2 Content (%) | --- |
Al2O3 Content (%) | --- |
MgO Content (%) | --- |
CaO Content (%) | --- |
Refractoriness (Degree) | Common (1580°< Refractoriness< 1770°) |
CrO Content (%) | --- |
SiC Content (%) | --- |
Model Number | CLT-A |
Brand Name | HuanXin |
Items | Content | ||
Submerged nozzle | Ladle nozzle | ||
SiO2 ≥% | 99.1 | 99.2 | |
ZrO2 ≥% | 75 | 75 | |
C ≥% | 10 | 10 | |
SiC ≥% | 5 | 5 | |
Al2O3 ≥% | 65 | 65 | |
A.P. %≤ | 14 | 15 | |
C.C.S. Mpa≥ | 46 | 45 | |
B.D. g/cm3≥ | 1.90 | 1.90 | |
Thermal shock≥ | 30 | 30 |