Fusible Polytetrafluoroethylene(PFA)
1. Product Introduction
Translucent particles or white powder. Molecular weight is 200,000～500,000; melting point is 300～310℃, friction coefficient is 0.05 (static friction coefficient, and steel grinding), specific gravity is 2.12～2.17, and melting index is 0.8～30. Long term use temperature 260℃.
Recommended for (but not limited to) chemical industry, aviation, aerospace industry, integrated processing materials.
2. Technical Parameter
Item | Technical Index | |||
FJY-A03/A03S | FJY-A06/A06S | FJY-A15/A15S | FJY-A30/A30S | |
Apprearance | Translucent particles or white powder，no impurities | |||
MFR,g/10min | 0.8～3.0 | 3.1～6.0 | 6.1～-15 | 15.1～-30 |
Tensile Strength,MPa ≥ | 32 | 30 | 28 | 22 |
Elongation at Break,% ≥ | 300 | 300 | 300 | 300 |
Water Content %, ≤ | 0.3 | |||
Melting Peak Temperature,℃ | 295～-315 | |||
Standard Specific Gravity | 2.120～2.170 | |||
3.Mark,Packing, Storage & Transportation
3.1Mark
There shall be firm and clear marks on the drums of this product, indicating company name, product name, batch number, brand number (specification number), net content, etc.
3.2 Package
The product is packaged in polyethylene plastic bags and then packaged in cardboard boxes with a net weight of 25 kg per box.
3.3Storage
It should stock in clean、cool、and dry warehouse, prevent from agglomeration and contamination.
3.4Transportation
This product is non-toxic, non-explosive, non-corrosive,according to non-dangerous goods transport.
4. Main Application
FYJ-A03:Can be used to make pipes, pumps, valves, plates, tank lining, diaphragm, joints and bearing parts.
FYJ-A06:Mainly used for pipe, wire insulation layer, film and various electronic components.
FYJ-A15:For extruding process, can manufacture cable insulation wire, multi-core cable sheath, etc.
FYJ-A30:Mainly used for the aerospace industry, chemical industry, faster cable extrusion, more economical for places that do not need high stress cracking.