High Cr Cast Iron Grinding Mill Liners Wear-resistance OEM
Quick Details
Ni-hard Discharge End Liners for Φ2.6m Rod Mill
1. Hardness: More than HRC53
2. International Standard: AS 2027-2002/Ni hard 1.
3. Microstructure: Eutectic Carbide + Martensite + Residual Austenite
Description:
Ni-hard Discharge End Liners for Φ2.6m Rod Mill
1. The Ni-hard End liners are used for grinding feldspar.
2. Hardness: More than HRC53.
3. International Standard:GB/T 8263-1999
AS 2027/Ni-Cr1-550
AS 2027/Ni-Cr2-500
AS 2027/Ni-Cr4-500
AS 2027/Ni-Cr4-600
AS 2027/Ni-Cr4-630
ASTM A 532 1-A,B,C,D
ASTM A 532 2-A,B,C,D,E
ASTM A 532 3-A
4. Microstructure: Eutectic Carbide + Martensite + Residual Austenite.
5. Heat treatment : Air quenching and tempering.
6. The liners are cleaned, sandblasted with a nice surface without any obvious visual defects.
7. Better wear performance & better reliability & cost effective in dry grinding process.
Product Details:
Application :Mine mill
Material :Ni-hard Cast Iron
Dimensions :As per drawings
Hardness :More than HRC53
Impact Value :More than 5J
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
|
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
|
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
|
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
|
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
|
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
|
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
|
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
|
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
|
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0.10~1.00 |
0.10~1.00 |
- |
- |
|
Ni |
≤0.50 |
≤0.30 |
0~0.30 |
0~0.30 |
0~0.30 |
- |
3.3~10 |
|
Re |
≤0.02 |
≤0.02 |
≤0.02 |
- |
- |
- |
- |
|
Equiva |