Description
Film: PVC Flex materials
Adhesive: Clear PSA
Backing: Douable sides PE and silicon coated,140gsm
Width: 1.24m
Length: 50m
Shelf Life: Up to 1 year at 20and relative humidity of 50%
Durability: Up to 1 year
Suit for: Common Applications
Solvent inkjet Eco solvent inkjet Traffic security signs
Cutting Advertisement signs
UV curable Fence advertisement
Screen printing
Physical Characters
Properties units Test method Average value
Thickness film with glue μm GB/T6672-2001 220±10
Weight- finished product g/m2 GB/T6672-2001 480±20
Gloss 60° % GB8807-88 60min
Initial Adhesion N/inch FINAT9 5min
180°Peel strength(steel,24h) N/inch FINAT1 10min
Dimensional stability MD mm FINAT14 1.5max
Dimensional stability CD mm FINAT14 1.0max
Elongation at break MD % GB/T1040.1-2006 100min
Elongation at break CD % GB/T1040.1-2006 500min
Tensile Strength at break MD N/25 mm GB/T1040.1-2006 200min
Tensile Strength at Break CD N/25 mm GB/T1040.1-2006 200min
Minimum application temperature°C + 10~35
Temperature range °C -20 ~ +70
Information on physical characteristics is based upon tests we believe to be reliable. The values
listed herein are average, minimum or maximum values. They are intended only as a source of
information and are given without guarantee and do not constitute a warranty. Purchasers should
independently determine, prior to use, the suitability of any material for their specific use.
All technical data is subject to change without prior notice. In order to avoid loss of quality, the
Zhongye product should be stored in suitable conditions, at temperature around 20 and relative
humidity of 50%. Under this condition, ZHONGYEproduct can be stored for period of 1 year.
When printing on Zhongye media, the temperature setting is very important, and we suggest
an optimum printing condition of 25°C, 50%.
Test Method:
Gross Degree:
Use a triangle gloss tester ,setting 60°given testing data is surface gloss of products.
Initial adhesion:
According to testing method (FTM-9,FINAT),remove release liner ,adhesive surface up ,make the specimen annular, to test peeling
strength after a quick, complete touch between the specimen and glass.
180°Peel strength(steel,24h):
(FTM-1, FINAT) is measured by peeling a specimen at a 180° angle from a stainless steel or float
glass panel, 24 hours after the specimenhas been applied under standardized conditions.
Initial adhesion is measured 20minutes afterapplication of the specimen.