Specifications:
| Item | Test conditions | Test method | Test data | unit |
| Density | ISO 1183:1987 | 1040 | kg/m3 | |
| Water absorption | ISO 62:1999 | <0.1 | % | |
| Melt flow rate | 200°C/5kg | ISO 1133:1997 | 3.8 | cm3/10min |
| Process shrinkage | ISO 294-4:1997 | 0.4-0.6 | % | |
| Charpy impact strength | 1eU | ISO 179:1993 | 15 | kj/m2 |
| Tensile modulus | 1mm/min | ISO 527-2:1993 | 3300 | MPa |
| Elongation | 50mm/min | ISO 527-2:1993 | 3 | % |
| Tensile strength at break | 50mm/min | ISO 527-2:1993 | 55 | MPa |
| Ball indentation hardness H | 358N/30s | ISO 2039-1:1993 | 150 | N/mm2 |
| Bending strength | 2mm/min | ISO 178:1993 | 100 | MPa |
| HDT | 1.8MPa | ISO 75-2:1993 | 84 | °C |
| Linear coefficient of thermal expansion | (23-80)°C | DIN 53 752 | 0.8-1.0 | K-1 |
| Heat conduction | DIN 52 612 | 0.16 | W/mK | |
| Vicat softening point | B50/oil | ISO 306:1994 | 93 | °C |
| Flame retardance | >1.4mm | UL-Standard 94 | 94HB | Class |
Application:
1.Food packaging.
2.Electrical industrial, instrumentation, communications equipment industry and other various instruments has been widely used as a shell, lamp, optical parts, equipment parts, transparent windows mirror, transparent model, acid, chemical storage tank, acid tank transport, telecommunications components, high frequency capacitors, high frequency insulation pads, brackets, inserts and frozen insulating materials.
3.All kinds of daily necessities,such as Plastic Cutlery, Toys.