Item | Unit | Outer layer | Middle layer, inner layer | Cover rubber sheet |
---|
Tensile strength at break | MPa | 14 | 12 | 6 |
Elongation at break | % | 400 | 400 | 250 |
Permanent deformation at break | % | 30 | 30 | 35 |
Hardness (shore A) |
| 55-65 | 50-60 | 55-65 |
Brittleness temperature | °C | -30 | -30 | -30 |
Hot water aging (100 °C × 96 h) | Tensile strength at break | MPa | 12 | 10 | 5 |
Elongation at break | % | 300 | 300 | 200 |
Hot water aging (70 °C × 96 h) | Tensile strength at break | MPa | 12 | 10 | 5 |
Elongation at break | % | 300 | 300 | 200 |
Volume expansion ratio | % | 15 | 15 | 15 |
Ozone aging: 10000 pphm, temperature 40 °C, stretching 20%, no cracking | min | 120 | 120 | 100 |
Wear loss (akron) | cm3/1.61 km | 1.0 | 1.0 | 1.2 |
Flexibility, no cracking | Ten thousand times | 20 | 20 | 20 |