Quick Detail:
Products: ASTM A295 51100 / SAE 51100 Stainless Bearing Steel Tube
Standard: GB / SKF/ ASTM / DIN / JIS / BS
Size(mm):
OD:8mm ~ 101.6mm
WT:1.0mm ~ 10mm
Length: Fixed(6m,9m,12,24m) or normal length(5-12m)
Description:
1. ASTM A295 52100 main features and application
ASTM A295 52100 is a kind of high-carbon chromium bearing steel. It has good synthesis performance.Quenching and tempering will make 52100 steel high and even hardness, and excellent abrasive resistance and fatigue strength. Good hot workability,after spheroidizing annealing, 52100 has good machinability, sensitive to white dot.
ASTM A295 52100 is mainly used to manufacture internal-combustion engine,electric locomotive,machine tool,tractor,steel rolling equipment,driller,steel balls,roller,and axle sleeve of rail truck, mining machine spiale.
2. The equal material of ASTM A295 52100 in different standard.
ASTM A295 |
GB/T18254 |
ΓOCT 801 |
ISO683-17 |
JIS G4805 |
DIN 17230 |
NF A35-565 |
52100 |
GCr15 |
IIIX15 |
1 |
SUJ2 |
100Cr 6 |
100Cr 6 |
ASTM A295 52100 chemical composition by %:
C |
Si |
Mn |
Cr |
Mo |
P |
S |
others |
0.95-1.05 |
0.15-0.35 |
0.25-0.45 |
1.4-1.65 |
≤0.1 |
≤0.025 |
≤0.02 |
Ni≤0.30 |
ASTM A295 52100 mechanical property and delivery condition:
Category |
Standard |
Delivery Condition |
Anneal (soften or spheroidizing ) hardness HBW |
Hot rolled bar |
ASTM A295 |
Hot rolled,hot rolled soften annealing,hot rolled spheroidizing annealing,hot rolled spheroidizing annealing skin,hot rolled soften annealing skin. |
179-207 |
Forging bar |
|||
Cold drawn bar |
Cold drawn or burnishing |
||
Hot rolled tube/pipe |
Hot rolled,hot rolled annealing burnishing |
||
Cold drawn tube/pipe |
Cold drawn |
||
Steel wire rod |
Hot rolled or spheroidizing annealing |
||
Wire |
Annealing |
Quenching HRC≥62 |
|
Wire |
Annealing |
φ≤10mm |
|
Phosphorus cold drawn |
φ≤10mm |
||
Cold drawn,burnishing |
-- |
||
Hot rolled or Forging bar,cold drawn bar and wire |
Hot rolled,cold drawn,annealing |
HBW 179-207 |
Applications:
1,Mainly used for ma