Flame Retardant Silicone Rubber Metal Banding for Tear Strength 49 kgf / cm
| Properties Test Report Compound E60D034X ASTM D2000 M2CA610A25B35EA14C32F17 | |||
| Original Properties | SPE Cification | TEST RESULT | ASTM Test Method |
| Hardness Shore A | 60°±5 | 58° | D2240 |
| Tensile Strength Mpa, Min | 10 | 10.9 | D412 |
| Ultimate Elongation %, Min | 250 | 488 | D412 |
| Tear Strength (kgf/cm) | 17 | 49 | D624 |
| SPE Cific Gravity (g/cm3) | 1.196 | D297 | |
| Heat Resistance 70H. AT 125℃ (A25) | D865 | ||
| Change in Hardness Points | +10 | +7 | |
| Change in Tensile Strength, Max % | -20 | +6.25 | |
| Change in Ultimate Elongation % | -40 | -35 | |
| Compression Set, Max, 22H. AT 100℃ (B35) | 70 | 51 | D395 Method B |
| Water Resistance: 100℃, 70H (EA14) | D471 | ||
| Change in Hardness Points | — | -1 | |
| Volume Change, % | ±5 | 2 | |
| Resistance to Ozone (C32) | No Crack | Pass | D1171 |
| Low-temperature, Brittleness (F17) | D2137 | ||
| Nonbrittle after 3 Min AT- 40℃ | Nonbrittle | Pass | |
| Conclusion: | |||
| Compound E60D034X Can Meet the Requirements of ASTM D2000 | |||
| M2CA610A25B35EA14C32F17 |
Details:
Silicone rubber metal bonded parts without excellent flexibility and good resistance to deformation, heat, oil, pressure, acid, abrasion, impact resistance, tensile strength, tear resistance, flame retardant, shock absorption, low temperature, anti-aging properties
Application:
Mainly used in automobiles, motorcycles, ships, coal, electric power, metallurgy, chemical industry, mining equipment and machinery manufacturing and other industries.To play a support, fixed, shock absorption, sealing and so on.