Nickel sheets, Nickel plate, Nickel foil
Grade: N2.N4,N5,N6,N7,Ncu30,Ncu40
Standard: ASTM B160,ASTM B161,ASTM B162
Size: 1. T0.3mm--4.0mm*W300-3000mm*L500-4500mm(Cold rolling)
2. T4.1mm--50.0mm*W300-3000mm*L500-4000mm(Hot rolling)
Technique: Cold rolled/Hot rolled
Inspection equipment: Nondestructive Tester; UT Testing Detector; Tensile Tester
Digital Ultrasonic Detector; Infrared Tester; HV Hardness Tester
Application: 1.Chemical processing, medical instruments etc.
2.Indusrty,Navigation,Smelting,Chemical plants, and so on.
Standard seaworthy package
Delivery: 25days after received the 30% deposit.
Nominal composition:
| Alloy | Ni% | Mn% | Fe% | Si% | Cu% | C% | Ti% |
| Nickel 200 | Min 99.2 | Max 0.30 | Max 0.2 | Max 0.10 | Max 0.20 | Max 0.10 | Max 0.10 |
| Nickel 201 | Min 99.2 | Max 0.30 | Max 0.2 | Max 0.10 | Max 0.20 | Max 0.02 | Max 0.10 |
Physical feature: Density in 700F 8.90 g/cm3; 0.322 ib./cu.in Linear expansion coefficient (Inch/Inch/0C) 20-100ºC 0.000014 20-200ºC 0.000014 Linear expansion coefficient (Inch/Inch/0C) 0.000015 20-700ºC 0.000016 Youngs modulus of elasticity,E,PSI×10-6 30.1 Conductivity 22.6% IACS Specific resistance in200C microhm.cm:7.63 ohms/cir.mil./ft.:45.9 Thermometric conductivity cal./cm.2sec.0C/cm.at700C:cal./cm.2sec.0C/cm.at700C:0.206 BTU/ft.2/hr./0F/ft.at 1580C:49.9 Temperature coefficient of resistance 200-1000C/0C 0.0058 200-5000C/0C 0.0074 200-8000C/0C 0.0060 Atomic number 28 Atomic weight 58.1 Atomic radius(A) 1.25 Crystal structuref.c.c Crystal constant(A) 3.52 Melting point 1.4530C; 2.6470F Boiling point 2.7300C;4.9500F Latent heat of fusion 73.8cal./g Specific heat at 200C-BTU/ib./0F 0.105 Interelectrode potential 0.25volts Velocity of sound 16.300ft./sec.;4.973m/sec. Poisson ratio 0.31 Thermal neutron cross section ( target ) absorption:4.6 Scatter:17.5 Magnetism: Curie temperature 3530C; 6650F Initial permeability 130 Maximum permeability 124 Saturation induction(B) 6050 Remnant induction(B) 3250 Diamagnetism(H) 3.0
|