General Description
Nickel 201 is a low carbon variety compared with Nickel 200, possessing low annealed hardness and a very low work-hardening rate, desirable for cold forming operations. It is highly resistant to corrosion by neutral and alkaline salt solutions, fluorine and chlorine, but in oxidizing salt solutions severe attack will occur.
The applications of pure nickel includes food and synthetic fiber processing equipment, electronic parts, aerospace and missile components, handling of sodium hydroxide above 300℃.
Chemical Composition (%)
Grade: Nickel 201
Ni: Min 99.90, Mn: Max 0.35, Fe: Max 0.4, Si: Max 0.35, Cu: Max 0.25, C: Max 0.02, S: Max 0.01
Designations
UNS N02201
worst-off Nr. 2.4068
Specifications
Nickel 201 Wire: ASTM B166
Nickel 201 Bar: ASTM B160
Nickel 201 Forging: ASTM B564
Nickel 201 Pipe: ASTM B161/B163/B725/B751
Nickel 201 Sheet/Strip: AMS B162
Physical Properties
Density：8.9g/cm3
Melting Point: 1435-1445℃
Electrical Resistivity: 0.085×10-6ohm.m
Thermal Conductivity: 79.3 W/m-K
Mechanical Properties
Tensile: Min 403 MPa
Yield: Min 103 MPa
Elongation: 50%