Product

Performance

Metal Fluorocarbon Painting Decorative Insulation

Board

Decoration

Layer

Ultrathin stone veneer decorative board

Multifunction, light weight, high strength, easy to install and  processing

High quality, low cost,  insulation, good decoration performance

Insulation Layer

EPS insulation layer

(Grade B1)

Heat conductivity ≤0.041.  volume-weight :18kg / m³ with the tensile strength:110--120kpa; volume-weight 20kg / m³ with the tensile strength :140kpa.

XPS insulation Layer

(Grade B1)

Heat conductivity ≤0.030. Volume-weight 25--45kg / m³ & tensile ≥150kpa. Strong compressive resistance.   30-40 years average using life. Excenllent structure load-bearing performance .

Polyurethane insulation board

(Grade B1)

Hard polyurethane with low thermal conductivity, good thermal performance. When the hard polyurethane with the  density of  35 ~ 40kg / m3, thermal conductivity is only 0.018 ~ 0.024w / (m.k), equivalent to  half of the EPS, is the lowest heat conductivity of all the insulation materials .

TPS insulation board

(Grade B1)

Heat insulation thermal conductivity is 0.060W / (m · k) ,it has good tensile compressive strength , impact resistance and stability ; its compressive strength reaches 150-500KPa

Rock wool  (Grade A)

Appearance quality: smooth surface, without prejudice practical scars, stains damaged. Combustion performance: non-combustible. Thermal load contraction temperature: 643 degrees.
Moisture absorption: 3.9%. Organic content: 2.9%.
Rockwool board basic parameters:
Material: rockwool
Apparent density: Rockwool 120 (kg / m3)
Heat conductivity: 0.04 (W / (m.K))
Max operating temperature: 80 (℃)
Specifications: 950,1150 (mm )
Operation standard: GB
Operating temperature: 80 (℃)

Phenolic Foam Board(Grade B Grade A)

Not be melt at high temperatures ,not be softened, with low smoke, non-proliferation flame resistance, flame penetration, There is  no distortion, no burning ,no fire, being placed 10 minutes at 1400 ℃, can effectively prevent the flames and smoke spread

Test Item

Detection standard and requirements

The third party test results

Coating thickness(μm)

GB/T13452.2-2008-10

≥30

199

Coating adhesion(MPa)

GB/T5210-2006

≥0.3

1.7(0.8-2.7),100%A

Hardness(Pencil)

GB/T6739-2006

≥4H

6H No scraping damage

Abrasive resistance(750g/500r),Suitable grinding wheel type:CS-10

GB/T1768-2006

0.003

Solvent resistance wiping(Butanone,100times)

HC/T-3792-2005

Appendix

No undercasing

Meet the requirement

Acid-resistance(5%HC1 liquor,24H)

GB/T9274-1998

No blistering,No Falling off,non-discolouring

No Change

Alkali resistance

GB/T9274-1998

No blistering,No Falling off,non-disco