1.very flexible and easy installation
ltable inner layer
3.operating temperature:-55+105
4.easily remove the tape upon inspection and maintenances
5.shrink ratio:30%
6.minimum fully recovery temperature:100
7.stndard color:red
hbit is made from radiation cross-linked polyolefin .the dual layer structure of insulation/hot melt adhesive effectively provides electric insulation and shock protection to busbar up to 24kv .widely used to protect irregular shape busbar or connectors where tube products can not be applied
Property | Test Method | Typical Data |
Tensile strength | ASTM D 2671 | ≥11.8MPa |
Tensile strength after aging | ASTM D 2671/120°C, 168hrs. | ≥10MPa |
Elongation at break | ASTM D 2671 | ≥550% |
Elongation at break after aging | ASTM D 2671/120°C,168hrs. | ≥450% |
Dielectric strength | IEC 243 | ≥20KV/mm |
Volume resistance | IEC 93 | ≥1013Ω.cm |
Dielectric constant | IEC250 | Max.3.0 |
Copper corrosion | ASTM D2671/120°C,168hrs. | No corrosion |
Water absorption | ISO 62/23°C,14days | <0.5% |
Product Dimensions (mm) |