Physical Properties | Nominal Value | |
Density g/cm3 | 0.921 | |
Melt Mass-Flow Rate (MFR) g/10min | 1.9 | |
Shore Hardness (shore D) | 45 | |
Tensile Modulus MPa | 175 | |
Tensile Strength MPa | Yield, | 9.0 |
Break, | 13.0 | |
Tensile Strain(Break) % | 850 | |
Modulus of Elasticity MPa | 250 | |
Vicat Softening Temperature°C | 89.0 | |
Melting Temperature (DSC) °C | 108 | |
Peak Crystallization Temperature (DSC) °C | 97.0 | |
Heat of Fusion J/g | 110 | |
Volume Resistivity ohm •cm | 8.5E+15 | |
Dielectric Strength kV/mm | 30.0 | |
Dielectric Constant (60Hz) % | 2.20 | |
Dissipation Factor (60 Hz) | 0.00050 | |