Spec Equivalents: Low Residual P (DLP)

The C12000 - Phosphorus – Deoxidized copper is high on thermal and electrical conductivity. These alloys can freely be formed using copper and possess 95% IACS conductivity, low residual phosphorus, and high embrittlement resistance. The alloy is available in the form of rod, tube, and wire.

Specifications:

ASME SB111	ASTM B152	ASTM B359	ASTM B506	ASTM B716
ASME SB133	ASTM B187	ASTM B372	ASTM B623	ASTM B743
ASME SB359	ASTM B188	ASTM B395	ASTM B638	ASTM B75
ASME SB395	ASTM B224	ASTM B42	ASTM B640	ASTM B88
ASME SB42	ASTM B272	ASTM B442	ASTM B641	MIL B-18907
ASME SB75	ASTM B280	ASTM B447	ASTM B68	MIL B-20292
ASTM B111	ASTM B302	ASTM B451	ASTM B687	MIL T-24107
ASTM B133	ASTM B306	ASTM B5	ASTM B698	MIL T-3235

Chemical Composition:

	Cu	Zn
Min/Max	99.9	0.5

Physical Properties:

Properties	US Customary	Metric
Density	8.89 g/cm3	0.321 lb/in3
Melting point	1083°C	1981°F
Tensile strength, ultimate	221 - 393 MPa	32100 - 57000 psi
Tensile strength, yield (depending on temper)	69.0 - 365 MPa	10000 - 52900 psi
Elongation at break ( in 101.6 mm (4 in.))	55.00%	55.00%
Machinability (UNS C36000 (free-cutting brass) = 100%)	20.00%	20.00%
Poisson's ratio	0.34	0.34
Elastic modulus	117 GPa	16970 ksi

Sizes Available:

HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS	8mm To 100 mm
HEX	10mm To 60mm
SQUARE	10mm To 60mm
FLAT	10mm Min Thickness and max Width 120mm
BILLETS	Up to 200 mm
INGOTS	As per Specification